The wire must be considered for oxidation, in order to prevent the formation of plastic deformation is not uniform to avoid failure in the course of the operation
As the protective gas oxidation increases, the amount of deoxidized elements (such as silicon, manganese, titanium, etc.) in the wire increases correspondingly, and the strength of the weld metal is reduced. When the deoxidation element in the wire contains the most insufficient, causing the weld toughness to decline, but also may lead to welding defects (such as pores, etc.) generation.
Welding hot-rolled steel, normalizing steel and welding under the use of low-carbon quenched and tempered steel, the first consideration of the mechanical properties of the weld metal and the base metal close to or similar to the weld metal chemical composition and the parent material is put In the secondary. In the welding of some large thickness, large binding of the components to prevent the emergence of welding cold cracks, may consider the principle of low matching, that is, the use of weld strength slightly lower than the base metal strength of the wire. Experience has shown that if the weld strength exceeds the base metal too much, the joint cold bending, plastic deformation is not uniform, resulting in cold angle is small, or even cracks.